The Main Process Of Tower Manufacturing
- Apr 05, 2018 -



  
Shearing
Shearing and cutting shall be performed carefully and all portions of the work which will be exposed to view after completion shall be finished neatly.  Manually guided cutting torches shall not be used.
   
Bending
Our company owaned the bending machince. Frether more, we can manufacture the towers with hot bending or cold bending according to client's requirements. 

Welding 
No welding shall be done unless prior approval has been obtained from the Engineer.
Welding shall not be allowed at tower attachment points for conductor, shieldwire, insulators or associated assemblies or brackets.
  
Sub-punching 
All holes in structural steel less than 10 mm thickness may be punched to full size unless otherwise noted on the approved Drawings.  Holes shown on the Drawings as drilled holes and all holes in structural steel 10 mm or more in thickness and tension members of crossarms shall be drilled or sub-punched and reamed.

Punching 
For punching to full size, the diameter of the punch shall be 1.0 mm larger than the nominal diameter of the bolt, and the diameter of the die shall not be more than 1.5mm larger than the diameter of the punch. For sub-punching, the diameter of the punch shall be 4 mm smaller than the nominal diameter of the bolt, and the diameter of the die shall be not more than 2 mm larger than the diameter of the punch.  Sub-punching for reamed work shall be such that after reaming no punch surface shall appear in the periphery of the hole.
 
Hole Size
Where holes are reamed or drilled, the diameter of the finished hole shall be not greater than the nominal diameter of the bolt plus 1.0 mm.
 
Galvanizing
All material shall be hot-dip galvanized after fabrication in accordance with the latest revision of GB/T 13912-2002 or ASTM Specification A 123. 
Material that has been rejected because of bare spots or other coating defects shall either be stripped and re-galvanized, or the uncoated areas shall be recoated by an approved method.
All plates and shapes which have been warped by the galvanizing process shall be straightened by being re-rolled or pressed.  The material shall not be hammered or otherwise straightened in a manner that will injure the protective coating.
  
Packing